Hydrodealkylation process

ABSTRACT

A novel catalyst system including an active metal oxide selected from the group consisting of noble metals and nickel; a promoter selected from the group consisting of tin and lead; if desired, a second promoter selected from the group consisting of alkali metals, such as potassium, rubidium, cesium, etc., an alkaline earth metal, such as calcium, strontium, barium, etc., and a rare earth metal, such as cerium, thorium, etc.; and an inert oxide support, such as alumina. The subject catalysts are utilized in the hydrodealkylation of alkyl aromatics, etc., in the dehydrogenation of paraffins and the like, and in the dehydrogenation-desulfurization of sulfur- and nitrogencontaminated hydrocarbon materials.

United States Patent Patrick et a].

[4 1 Aug. 22, 1972 [54] HYDRODEALKYLATION PROCESS [72] Inventors: Ralph E. Patrick, Flatwoods; Ronald A. Kmecak; Stephen M. Kovach,

[21] Appl. No.: 769,737

[52] US. Cl ..260/672 R, 208/112, 208/138, 208/143, 252/457, 252/459, 252/460,

[51] Int. Cl. ..C07c 3/58, C07c 1l/04, C07c 5/18,

ClOg 23/02 [58] Field of Search ..260/672, 683.3, 673.5

[56] References Cited UNITED STATES PATENTS 3,124,526 3/ 1 964 Butler ..208/264 3,21 1,669 10/ 1965 Unverferth ..252/416 3,258,431 6/ 1966 Fisher et al. ..252/457 3,446,869 5/1969 Nolan ..260/680 3,448,165 6/1969 Bloch ..260/683.3 3,461,177 8/ 1969 Box et al ..260/673.5 3,477,944 11/1969 Van Driesen ..208/143 3,480,531 11/1969 Mulaskey ..208/143 3,494,857 2/1970 McIlvried ..208/ 143 2,734,929 2/1956 Doumani ..260/ 672 2,861,959 1 1/1958 Thorn et al. ..252/465 3,511,888 5/1970 Jenkins ..260/683.3 X

3,399,132 8/1968 Mulaskey ..208/1 1 1 3,002,920 10/1961 Porter et al ..208/138 3,531,543 9/1970 Clippinger et al. .....260/683.3

3,306,944 2/ 1967 Pollitzer ..260/672 OTHER PUBLlCA'l'lONS page 208- 19 (Sept. 1958) Classification Definitions Primary Examiner-Delbert E. Gantz Assistant Examiner-G. E. Schmitkons AttorneyWalter H. Schneider [57] ABSTRACT A novel catalyst system including an active metal oxide selected from the group consisting of noble metals and nickel; a promoter selected from the group consisting of tin and lead; if desired, a second promoter selected from the group consisting of alkali metals, such as potassium, rubidium, cesium, etc., an alkaline earth metal, such as calcium, strontium, barium, etc:, and a rare earth metal, such as cerium, thorium, etc., and an inert oxide support, such as alumina. The subject catalysts are utilized in the hydrodealkylation of alkyl aromatics, etc., in the dehydrogenation of parafiins and the like, and in the dehydrogenationdesulfurization of sulfurand nitrogen-contaminated hydrocarbon materials.

4 Claims, N0 Drawings HYDRODEALKYLATION PROCESS BACKGROUND OF THE INVENTION The present invention relates to novel catalyst compositions, particularly useful for the catalysis of hydrogen transfer reactions and novel processes for the utilization of such catalysts. In a more specific aspect, the present invention relates to novel catalyst compositions particularly useful for the conduct of hydrodealkylation reactions, dehydrogenation reactions, and hydrogenation-hydrotreating reactions, and such reactions utilizing these catalysts.

In recent years, the demand for hydrocarbon fuels and chemicals derived from hydrocarbons has increased at such a rapid rate and the domestic supply of petroleum crude oils had diminished to the point that it has become necessary to convert low grade petroleum crude oils to fuels and chemicals, to upgrade refinery streams not heretofore utilized for high grade fuels and chemicals and to utilize hydrocarbon liquids, also usually of low grade, derived from coal by carbonization and solvent extraction, from oil shales, and from tar sands. One of the primary operations for the upgrading of low grade hydrocarbons is a group of reactions involving changing the carbon to hydrogen ratio or displacing a substituent group with hydrogen. The change in the carbon to hydrogen ratio may be effected by dehydrogenation as, for example, in the dehydrogenation of paraffins to corresponding monoolefins, in the dehydrogenation of paraffins and monoolef'ms to di-olefins; or in the dehydrogenation of paraffins or cycloparaffins to aromatics, or the change may be effected by hydrogenation as, for example, in the hydrogenation of diisobutylene to isooctane and in the hydrogenation of unsaturated polymer gasoline into motor fuels of less unsaturated character and the like. In certain instances, such changes in the carbon to hydrogen ratio may be accompanied to some extent by isomerization type reactions, such as those involved in the cyclization of paraffinic hydrocarbons, such as the conversion of hexane to benzene, etc. In some instances, also, the hydrogen displaces substituent groups, particularly substituent groups of cyclic hydrocarbons; for example, in the dealkylation of alkyl aromatics, etc. Destructive conversion of organic sulfur and nitrogen compounds found in some hydrocarbon materials and the saturation of highly unsaturated materials may also be effected.

One particularly useful reaction of this type is the hydrodealkylation of alkyl aromatics to convert toluene to benzene, and coal tar light oils and coal tar methyl naphthalene to benzene and naphthalene, respectively. The thermal version of this process requires extremely high temperatures and pressures. The catalytic process generally employs a chromiamagnesia catalyst deposited on an alumina base, but, in spite of the efiectiveness of this catalyst, it requires high temperatures, high hydrogen pressures and sufl'ers from low yields, low selectivity and rapid degeneration of the catalyst.

Another highly valuable reaction of this character is a dehydrogenation process which converts paraffins to olefins, etc. While several processes have been developed for this purpose, these processes have very short on-stream times, they are cyclic, adiabatic, fixedbed operations and necessitate frequent regeneration of the catalyst due to carbon lay-down and catalyst fouling. Catalyst deactivation is also quite pronounced.

Another process of extreme importance when dealing with low grade hydrocarbon liquids, particularly those containing substantial volumes of sulfur and nitrogen and their compounds is the hydrogenationhydrotreating of such materials. While certain catalysts have heretofore been developed for this type of operation, none appear to have qualities necessary to simultaneously desulfurize and denitrogenate the crudes and add hydrogen to the aromatic and olefmic compounds contained in the feed materials. In other words, some catalysts have heretofore been useful in desulfurizing and denitrogenating but are highly ineffective for the hydrogenation portion of the reaction; whereas, those useful for hydrogenation are readily poisoned by the desulfurization and denitrogenation. Again, in this area of operation, there is a tendency for the catalyst to rapidly degenerate and become coked, thereby losing its activity quite rapidly.

It is therefore an object of the present invention to provide an improved catalyst for overcoming substantially all of the above mentioned difficulties. In a more specific aspect, the present invention relates to a novel catalyst system for carrying out hydrogen transfer reactions. Still another object of the present invention is to provide an improved catalyst system for hydrogen transfer reactions which requires relatively low temperatures. Another object of the present invention is to provide an improved catalyst system for hydrogen transfer reactions which requires relatively low hydrogen pressures. Another object of the present invention is to provide an improved catalyst system for hydrogen transfer reactions which produce high product yields. Another and further object of the present invention is to provide an improved catalyst system for hydrogen transfer reactions which exhibits a high selectivity to the desired reaction. Yet another object of the present invention is to provide an improved catalyst system for hydrogen transfer reactions which is highly resistant to coking. Another object of the present invention is to provide an improved catalyst system and process for the hydroalkylation of alkyl aromatics. Another and further object of the present invention is to provide an improved catalyst system and process for the dehydrogenation of paraflmic hydrocarbons. Still another object of the present invention is to provide an improved system and process for the hydrogenation-dehydrogenation of hydrocarbon materials contaminated with sulfur and nitrogen. These and other objects and advantages of the present invention will be apparent from the following description.

SUMMARY OF THE INVENTION Briefly, in accordance with the present invention, the novel catalyst composition of the present invention includes an active metal of Group VIII selected from the group consisting of noble metals and nickel, a promoter of a Group IV metal selected from the group consisting of tin and lead and an inert carrier material. More specifically, the noble metals of Group VIII, and nickel, in their oxide forms are deposited on an inert oxide carrier along with tin or lead in their oxide form. The catalysts are further improved by adding to the Group VIII and Group IV metals an. alkali metal, an alkaline earth metal, or a rare earth metal as a second promoter. Novel hydrogen transfer reactions utilizing the above catalytic materials are also taught herein.

The novel catalysts of the present invention include a Group VIII metal in its oxide form, including specifically ruthenium, rhodium, palladium and platinum of the noble metal group, and nickel from the non-noble metal or ferrous group of Group vm. The promoter from Group IV particularly includes tin and lead oxides. Where a second promoter is utilized, a metal selected from the group consisting of alkali metals, alkaline earth metals and rare earth metals may be utilized. These materials are also in their oxide forms and include potassium, rubidium, cesium, calcium, strontium, barium, cerium, thorium, and the like. The inert oxide support is preferably a gamma alumina, including the beta, eta, boehmite and bayerite, etc., crystalline forms. Other inert oxide supports include other aluminas, silica-alumina, silica, silica-magnesia, aluminamagnesia, silica-zirconia, etc.

In the preparation of the novel catalysts of the present invention, well-known techniques may be employed. These include, for example, coprecipitation and impregnation techniques. The base material may be an extrudate or pellet to be impregnated or a powder which is thereafter pelletized or extruded to yield the finished catalyst. The active metal portion of the catalyst and the promoters are added through the use of water-soluble salts such as their halides, nitrates, sulfates, acetates, etc. Easily hydrolyzed salts can be kept in solution without decomposition by employing an appropriate inorganic acid, for example, sulfuric acid for tin sulfate, hydrochloric acid for tin chloride, etc. Drying and calcination of the catalyst can be employed, for example vacuum drying, and calcination in oxidative, neutral or reductive atmospheres employing temperatures of about 800 to -1,200 F.

The following examples are illustrative of accepted techniques for preparing the novel catalysts of the present application EXAMPLE I To 900 ml. of distilled water was added 40 g. of stan' nous sulfate and ml. of concentrated sulfuric acid. The sulfuric acid was required to bring the insolubles from the stannous sulfate into solution. This was believed to be tin hydroxide. This solution was added to 900 ml. of a boehmite alumina as pellets and after contact for fifteen minutes, the unadsorbed liquid was decanted from the catalyst pellets. The resulting impregnated catalyst was dried at 250 F for 1 hour and calcined in air at 950 F in a muffle furnace for 16 hours. This yielded a catalyst of the following composition:

2 percent SnO-AhO A solution containing 150 ml. of distilled water and 2 I g. of rhodium trichloride was added to 150 ml. of 2 percent SnOAl O pellets from above. Catalyst and solution was in contact for 15 minutes and the unadsorbed liquid was decanted. The resulting catalyst was dried at 250 F for 1 hour and calcined in air at 950 F in a muffle furnace for 16 hours. This yielded a catalyst of the following composition:

1 percent Rh2percent SnOAl O A solution containing 150 ml. of distilled water and 5.5 g. of cesium nitrate was added to 150 ml. of l per- 1 percent Rh2 percent Cs O2 percent SnO-AI O EXAMPLE II By employing the techniques and procedures outlined in Example I, other catalytic compositions were prepared. A solution containing ml. of distilled water and 67 g. of a 5 percent palladium (ous) chloride solution was added to 15 0 ml. of 2 percent SnO-Al O pellets rsdin fiss nslql- Dry nslsa in n yielded thefollowing composition:

1 percent Pd--2 percent SnO-Al O A solution containing 150 ml. of distilled water and 5.5 g. of cesium nitrate was added to 150 ml. of lpercent Pd-2 percent SnOAl O pellets from above. Drying and calcination yielded the following composition:

1 percent Pd2 percent Cs O-2 percent SnO-Al O EXAMPLE III To 600 ml. of distilled water was added 54 g. of stannous sulfate and 20 ml. of concentrated sulfuric acid. The tim sulfate was partially insoluble and the sulfuric acid brought it into solution. This insolubility was probably due to the presence of tin hydroxide. This solution was added to 600 ml. of a boehmite alumina and after contact for 15 minutes the unadsorbed liquid was decanted from the catalyst pellets. The resulting impregnated catalyst was dried at 250 F for 1 hour and calcined at 950 F in air in a muffle furnace for 16 hours. This yielded a catalyst of the following composition:

4 percent SnOAl O;,

A solution containing 150 ml. of distilled water and 4.5 g. of chloroplatinic acid was added to 150 ml. of 4 percent SnOAl- O pellets (prepared as above) and allowed to remain in contact for 15 minutes before decanting the unadsorbed liquid. The impregnated catalyst was dried at 250 F for 1 hour and calcined in air at 950 F for 16 hours in a mufi'le furnace. This yielded a catalyst of the following composition:

1 percent Pt-4 percent SnOAl O EXAMPLE IV By employing the technique and procedure outlined in Example III, 1 percent Rh-4 percent SnOAl O and 1 percent Ru--4 percent SnO-Al 0 were prepared by utilizing rhodium trichloride and ruthenium trichloride, respectively.

Optimum contents of the Group VIII metal include 0.5 5 percent by weight based on the finished catalyst,

while the promoter concentration varies between 1 and 15 percent by weight.

As previously pointed out, the catalysts of the present application are-particularly useful in carrying out the hydrodealkylation of alkyl aromatics to produce the parent aromatic hydrocarbons. F eedstocks for such process include toluene and polymethyl benzenes, coal tar light oils, coal tar methyl naphthalene concentrates, and bicyclic concentrates from light cycle oils and heavy reformates. Feedstock preparation can include fractionation to remove front ends or bottoms, thereby removing undesired fractions, such as unsaturates, indanes and resinous materials. The distillation may be preceded or followed by a hydrogenation-hydrotreating step. Feedstocks with or without sulfur can be processed over the catalysts of the present invention. It is preferred, however, to employ a trace of sulfur to 100 ppm.) in order to reduce hydrocracking activity without hindering the hydrodealkylation activity of the catalyst.

The processing conditions for the hydrodealkylation reaction of the present invention include a temperature between about l,050 and l,200 F, a pressure between about 100 and 1,000 psig., a liquid hourly space velocity between about 0.1 and 5, and a hydrogen-tohydrocarbon mole ratio of about 3 to 1.

In order to illustrate the hydrodealkylation ability of the catalysts of the present invention, a series of Runs was made in which toluene was hydrodealkylated at 1,150 F, 500 psig., 0.5 LHSV, and a 5:1 hydrogen to hydrocarbon ratio. The Table below gives the results of these Runs as compared with runs utilizing a commercial chromia-magnesia on alumina catalyst.

TABLE I Run 1 2 3 4 5 6 7 Catalyst lRhl2Cr- 2Cs 2Mg- 28n- Al,0 Al,0,,

Feed

Sulfur, PP Liquid recovery Vol.

$. 9 wand The chromia-magnesia catalyst used in the comparison is a commercial hydrodealkylation catalyst which is probably the most widely used in the industry. It is apparent, however, that catalysts of this invention result in higher conversion rates at comparable selectivities and have lower coking rates. The lower coking rates, of course, insures longer on-stream catalyst life and lower operating temperatures. The true coking rate of the commercial catalyst is not evident from the data. In actual practice, this catalyst is completely deactivated by coke within several days and to maintain conversion, operating temperatures must be raised at about 1,300-1,350 F as the catalyst ages. Secondly, high hydrogen partial pressures must be maintained to control the increase in coking with elevation in operating temperatures. By contrast, the catalysts of the present invention maintain a low coking rate, conversion remains constant with carbon deposition on the catalyst, the lower hydrogen ratios can be utilized.

In other studies of the above catalysts, it was found that coal tar methylnaphthalene concentrates, as received from the coke oven, contain large amounts of resinous materials. However, by distilling these concentrates to yield a percent overhead fraction, polymers, resins and free carbon may be removed as a bottoms fraction. By thus pretreating these concentrates, the carbon lay-down on the hydrodealkylation catalyst is further reduced and hydrogen consumption due to hydrocracking of the resins and polymers is reduced.

The following Table II illustrates the efiect of a catalyst of the present invention as compared with a commercial chromia-magnesia catalyst when utilized in the hydrodealkylation of coal tar methylnaphthalenes. The conditions employed included a temperature of 1,100 F, a pressure of 500 psig., a liquid hourly space velocity of 0.5 and a hydrogen-to-hydrocarbon mole ratio of 5: 1.

Table III shows the use of a catalyst of this invention on a different feed under the same conditions.

TABLE III Run l0 Catalyst Pt-SnOALO, Feed Toluene 5 1.6 Naphthalene 48.3

Me Naphthalene Di Me Naphthalene The advantages of the process of the present invention are further illustrated by a series of tests conducted for thehydrodealkylation of toluene in the presence of the novel catalysts of the present invention. Specifically, in the tests set forth in the following Table, a noble metal was combined with lead in one instance and this catalyst thereafter had a rare earth metal added thereto in a second test.

TABLE IV Conditions: 1150F, 500 PSIG, 0.5 LHSV, /1 HJH'C Feed: Toluene Another hydrogen transfer process in which the novel catalysts of the present invention are highly successful is the dehydrogenation reaction. More specifically, the preferred process involves mono-olefin preparation by the dehydrogenation of corresponding paraffins. While this is a comparatively simple process, the on-strearn time is generally very short, between about 7 to 15 minutes, and cyclic, adiabatic, fixed-bed reactors are necessary with frequent regeneration of the catalyst due to the coke lay-down. For continuous operation, therefore, several reactors are required in parallel; one on-stream, one being regenerative and one on standby. Multiples of this arrangement can also be utilized;

Briefly, in accordance with this phase of the present invention, paraffins are dehydrogenated to produce olefins and hydrogen. Suitable feedstocks for use in accordance with the presentinvention include ethane, propane, normal butane, iso-butane, normal pentane, iso-pentane etc.

Processing conditions are dependent upon the feedstock employed. Generally, temperatures between about 900 and 1,250 F, pressures between about 100 mm. and 2,500 mm. mercury absolute, and liquid hourly space velocities from about 0.1 to 10 may be employed. More specifically, if ethane is the feedstock, the temperature should be between about 1,100 and 1,250 F. Where C to C parafiins are the feedstock, a temperature of 900 to 1,150 F should be used.

The effectiveness of the catalysts of the present in vention is illustrated by the results set forth in the following Table wherein propane was dehydrogenated at 1,110 F, 810 mm. mercury absolute, 5 LHSV and using an 88-minute cycle. Runs 1 1 through 14 show the results of Runs with unpromoted noble metal catalysts and runs 20 and 21 show other Group VIII metals of the ferrous group.

TABLEV Run 13 14 15 l6 l7 l8 Cata- 0.5Pt- 0.6Pt- 0.6PtlRhlyst 0.5Ru lPd 0.5Rh 0.6Pt 4Sn 1Pt'2Cs A1 0, Al,0, Al,0, A1,0, AI,O, 4Sn-AI,,O Conversion 11.! 13.5 15.1 13.3 15.4 12.5 Selectivity 75.3 62.2 71.1 75.6 93.5 90 AConversion 0 3.6 5.3 9.8 0 0 Gm. Coke 20g. catalyst 0.22 0.41 0.63 0.38 0.27

Mole H, 14.3 14.6 15.9 14.5 17.6 15.3 Methane 1.1 2.0 1.7 1.3 0.4 0.5 Ethane 1.1 2.0 1.7 1.3 0.4 0.5 Hz Purity 73 79 82 95.5 93.5

Run 19 20 21 22 23 5Ni- 10Ni- 10Ni- 10Co- 10Fe- Catalyst 2K 2K 4Sn 2K 2K 4Sn- 4Sn- A1,0 4Sn- 4Sn- Al,0, A1,0, ALO, Al O, Conversion 20.5 18.2 24.0 No Activity Selectivity 92.5 94.8 91.3 AConversion 0 0.5 6.4 Gm. Coke 20 g. catalyst 0.16 0.25 0.08 Mole H, 19.1 19.2 22.6 Methane 0.6 0.4 0.8 Ethane 0.6 0.4 0.8 H, Purity 93.7 95.9 93.2

It is obvious from previous tests that the catalysts of the present invention give higher conversion rates, and equal or better selectivities with lower deactivation rates than the better of the commercial catalysts. These improved selectivities and deactivation rates appear to be due to the low coking rates of the catalysts of the present application. It is also to be observed from the previous Table that iron and cobalt showed no activity for the dehydrogenation reaction; hence, the ferrous group metals of the present invention are limited to nickel.

Another highly valuable reaction which can be carried out for the use of the novel catalyst of the present invention is a combined hydrogenation-hydrotreating operation. In this area, nickel molybdate and cobalt molybdate on alumina are generally used for hydrogenation-denitrogenation or hydrogenationdesulfurization, respectively. While these catalysts are, in essence, hydrotreating catalysts, their activity is therefore principally the removal of sulfur and nitrogen contaminants and to a lesser extent, hydrogenation. On the other hand, an excellent hydrogenation catalyst is platinum deposited on alumina. However, this catalyst is easily poisoned by the impurities which are to be removed by the previously mentioned catalysts; namely, sulfur, nitrogen, etc. Therefore, in the past, it has been necessary to utilize several catalytic treatments in order to effect hydrogenation-hydrotreating. In accordance with the present invention, it has been found that the improved catalysts of this invention are highly effective for hydrogenation-hydrotreating to simultaneously hydrogenate unsaturates and remove contaminants such as sulfur, nitrogen, etc., and that such catalysts have a low coking rate.

Feedstocks which may be processed over the catalysts of the present invention in a hydrogenationhydrotreating operation include petroleum hydrocarbons from crude oil such as naphthas, kerosene, light and heavy cycle oils, gas oils, residuals, asphalts, etc.; shale oil derived fractions; liquids derived from the pyrolysis or carbonization of coal, such as coal tar liquids, and liquids obtained from the solvent extraction of coal.

Suitable conditions for the operation of the hydrogenation-hydrotreating process of the present invention include a temperature of about 500 to 900 F, a pressure of about 100 to 3,000 psig., a liquid hourly space velocity between about 0.1 and 10, and a hydrogen-to-hydrocarbon mole ratio of about 3 to 15/1.

When reference is made herein to the Periodic System of elements, the particular groupings referred to are as set forth in the Periodic Chart of the Elements in The Merck Index, Seventh Edition, Merck & Co., lnc., 1960.

What is claimed is:

l. A process for treating hydrocarbon materials to effect hydrodealkylation of alkyl aromatic hydrocarbons as the predominant reaction, comprising; contacting the hydrocarbon materials with a catalyst consisting essentially of an active metal selected from the group consisting of about 0.5 to 5 percent by weight of a noble metal and about 1 to 15 percent by weight of nickel and about 1 to 15 percent by weight of a metal selected from the group consisting of tin and lead both deposited on a gamma alumina support and maintaining conditions sufiicient to effect said hydrodealkylation.

2. A process in accordance with claim 1 wherein the tin and lead are in their oxide form.

3. A process for treating hydrocarbon material to effect hydrodealkylation of alkylaromatic hydrocarbons as the predominant reaction, comprising; contacting the hydrocarbon with a catalyst consisting essentially of an active metal selected from the group consisting of about 0.5 to 5 percent by weight of a noble metal and about 1 to 15 percent by weight of nickel, about 1 to 15 percent by weight of a metal selected from the group consisting of tin and lead, and about 1 to 15 percent by weight of an additional promoter selected from the group consisting of an alkali metal, and alkaline earth metal, a rare earth metal, and mixtures thereof all deposited on a gamma alumina support and maintaining conditions sufficient to effect said hydrodealkylation.

UNITED sTATEs PATENT OFFICE CERTIFICATE 0F CORRECTlUN Patent No. 3,586,340 Dated Auqust 22, 1972 Irwentor(5) Ralph E. Patriok RnnalrLA Kmpruak I and Stephen M4 Knvaoh It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

In Column 4, line 36; "tim" should be corrected to tin In Column 6 line 8; "at" should be corrected to to line 51;

30.4" should appear in Column 8 of Table II.

In Column 7 line 3; "47 .3" should appear in the column headed "52 .4"

In Column 10, line 14; "material" should read materials In Column 10, after Claim 3 add Claim 4 as follows:

4. A process in accordance with Claim 3 wherein the additional promoter is in its oxide form.

(SEAL) Attest:

ROBERT GOT'I'SCHALK EDWARD M.FLETCHER, JR.

Commissioner of Patents Attesting Officer USCOMM-DC 60376-P69 FORM PO-105O (10-69) Us. GOVERNMENT PRINTING OFFICE was 0-366-334 

2. A process in accordance with claim 1 wherein the tin and lead are in their oxide form.
 3. A process for treating hydrocarbon materials to effect hydrodealkylation of alkylaromatic hydrocarbons as the predominant reaction, comprising; contacting the hydrocarbon with a catalyst consisting essentially of an active metal selected from the group consisting of about 0.5 to 5 percent by weight of a noble metal and about 1 to 15 percent by weight of nickel, about 1 to 15 percent by weight of a metal selected from the group consisting of tin and lead, and about 1 to 15 percent by weight of an additional promoter selected from the group consisting of an alkali metal, and alkaline earth metal, a rare earth metal, and mixtures thereof all deposited on a gamma alumina support and maintaining conditions sufficient to effect said hydrodealkylation.
 4. A process in accordance with claim 3 wherein the additional promotor is in its oxide form. 